I need help id/ naming parts and years they are form. I'd like to figure out the "correct" name of parts ( I am just calling them chevy nose...
sure it's possible to have small scraps left over after I layout cut out the seat parts but at that point I am commented as the sheet of material...
yep it is hard stuff , we use it for the skin old style riveted airboats and can beat the tar out of them normally bending the T bar stringers...
It's little thinker then I'd like for this at 0.90 but its what I have so I guess they will be stout bomber seats :) 1/2" radius is way better...
sorry about that yes 7075 T6 . I guess what I am trying to get at is what are ya'll calling a "large" radius? I know it rolls a 4" radius...
Not worried about welding it I have plenty of solid aircraft rivets to give it some character How lazy of a curve have you done in your bead...
yes I agree, if I was going to BUY another sheet of material a softer alloy like 5052 or 3003 would have been much better to use however the key...
Thanks, this was my concern to. I guess I should not always think about using stuff just cause I have it Maybe this is just wishful thinking...lol
I am wondering if anyone else has tried to use 7075 aluminum in a bead roller to do things like a 1.5" round over or the wire edge on top of a...